Magnetic diffusion anomaly at the Neel temperature of pyrrhotite, Fe1-xS

TitleMagnetic diffusion anomaly at the Neel temperature of pyrrhotite, Fe1-xS
Publication TypeJournal Article
Year of Publication2015
AuthorsF. Herbert, W, Krishnamoorthy, A, Rands, L, Van Vliet, KJ, Yildiz, B
JournalPhysical Chemistry Chemical Physics
Volume17
Issue16
Pagination11036 - 11041
Date Published2015///
Abstract

Cation diffusion is an important rate-limiting process in the growth of pyrrhotite (Fe1-xS) in passivating films on steels exposed to sulfidic environments, and for proposed synthetic applications of Fe1-xS, for example single-phase magnetic switching devices. Above the Neel temperature T-N of 315 degrees C, where Fe1-xS is paramagnetic and structurally disordered, iron self-diffusivity *D-Fe predictably follows a standard, established Arrhenius law with temperature. However, we report Fe-57 tracer diffusion measurements below T-N, obtained using secondary ion mass spectrometry (SIMS), that demonstrate a 100-fold reduction in diffusion coefficient as compared to the extrapolated, paramagnetic Arrhenius trend at 150 degrees C. The results can be described by a magnetic diffusion anomaly, where the vacancy migration energy for the spontaneously-magnetized cation sublattice is increased by approximately 40% over the paramagnetic state. These constitute the first set of consistent diffusivity data obtained in magnetic pyrrhotite, allowing more accurate prediction of pyrrhotite growth rates and determination of magnetic properties for synthetic devices.